Electrodepositable coating compositions and method for improved cure response

ABSTRACT

An improved electrodepositable composition is provided comprising: (a) an active hydrogen-containing cationic resin electrodepositable on a cathode; (b) a capped polyisocyanate curing agent; and (c) an organotin-containing catalyst. The improvement comprises the addition to the electrodepositable composition of a water immiscible acid functional compound having a hydrocarbon chain of at least 5 carbon atoms like abietic acid and natural sources thereof. A preferred acid functional compound is abietic acid. The composition provides improved cure response and appearance properties when electrodeposited over conductive substrates.

BACKGROUND OF THE INVENTION

This application is a continuation-in-part of U.S. patent application Ser. No. 08/329,106, filed on Oct. 25, 1994, now abandoned and Ser. No. 08/820,827 has been filed as a continuation thereof on Mar. 19, 1997.

FIELD OF THE INVENTION

The present invention relates to cationic electrodepositable compositions, and to their use in electrodeposition.

BACKGROUND OF THE INVENTION

The application of a coating by electrodeposition involves depositing a film-forming composition to an electrically conductive substrate under the influence of an applied electrical potential. Electrodeposition has gained prominence in the coatings industry because in comparison with non-electrophoretic coating methods, electrodeposition provides higher paint utilization, outstanding corrosion resistance, and low environmental contamination. Early attempts at commercial electrodeposition processes used anionic electrodeposition, where the workpiece being coated served as the anode. However, in 1972, cationic electrodeposition was introduced commercially. Since that time, cationic electrodeposition has become increasingly popular and today is the most prevalent method of electrodeposition. Throughout the world, more than 80 percent of all motor vehicles manufactured are given a primer coating by cationic electrodeposition.

Many cationic electrodeposition compositions used today are based on active hydrogen-containing resins derived from a polyepoxide and a capped polyisocyanate curing agent. These cationic electrodeposition compositions contain organic tin catalysts such as dibutyl tin oxide to activate cure of the electrodeposition composition. Because of cost and environmental considerations, the levels of these tin catalysts are kept low. Organotin catalysts are relatively expensive and appear in the ultrafiltrate of electrodeposition baths, which can present waste disposal problems. However, low catalyst levels may lessen the cure response of a coating composition, providing weaker properties in the cured film than desired. Appearance of the cured film may also be adversely affected.

It would be desirable to provide an electrodepositable composition which demonstrates enhanced cure response at low organotin catalyst levels without loss of cured film properties including humidity resistance, adhesion, and appearance.

SUMMARY OF THE INVENTION

In accordance with the present invention, an improved electrodepositable composition and a method of electrodeposition using the composition are provided. The electrodepositable composition comprises (a) an active hydrogen-containing cationic resin electrodepositable on a cathode; (b) a capped polyisocyanate curing agent; and (c) an organotin-containing catalyst. The improvement comprises the addition to the electrodepositable composition of at least one water immiscible acid functional compound having a hydrocarbon chain of at least 5 carbon atoms. The water immiscible acid functional compound is preferably polycyclic.

DETAILED DESCRIPTION

The cationic resin of the present invention is preferably derived from a polyepoxide and can be prepared by reacting together a polyepoxide and a polyhydroxyl group-containing material selected from alcoholic hydroxyl group-containing materials and phenolic hydroxyl group-containing materials to chain extend or build the molecular weight of the polyepoxide. The reaction product can then be reacted with a cationic salt group former to produce the cationic resin.

A chain extended polyepoxide is typically prepared as follows: the polyepoxide and polyhydroxyl group-containing material are reacted together neat or in the presence of an inert organic solvent such as a ketone, including methyl isobutyl ketone and methyl amyl ketone, aromatics such as toluene and xylene, and glycol ethers such as the dimethyl ether of diethylene glycol. The reaction is typically conducted at a temperature of about 80° C. to 160° C. for about 30 to 180 minutes until an epoxy group-containing resinous reaction product is obtained.

The equivalent ratio of reactants; i.e., epoxy:polyhydroxyl group-containing material is typically from about 1.00:0.50 to 1.00:2.00.

The polyepoxide preferably has at least two 1,2-epoxy groups. In general the epoxide equivalent weight of the polyepoxide will range from 100 to about 2000, typically from about 180 to 500. The epoxy compounds may be saturated or unsaturated, cyclic or acyclic, aliphatic, alicyclic, aromatic or heterocyclic. They may contain substituents such as halogen, hydroxyl, and ether groups.

Examples of polyepoxides are those having a 1,2-epoxy equivalency greater than one and preferably about two; that is, polyepoxides which have on average two epoxide groups per molecule. The preferred polyepoxides are polyglycidyl ethers of polyhydric alcohols such as cyclic polyols. Particularly preferred are polyglycidyl ethers of polyhydric phenols such as Bisphenol A. These polyepoxides can be produced by etherification of polyhydric phenols with an epihalohydrin or dihalohydrin such as epichlorohydrin or dichlorohydrin in the presence of alkali. Besides polyhydric phenols, other cyclic polyols can be used in preparing the polyglycidyl ethers of cyclic polyols. Examples of other cyclic polyols include alicyclic polyols, particularly cycloaliphatic polyols such as 1,2-cyclohexane diol and 1,2-bis(hydroxymethyl)cyclohexane. The preferred polyepoxides have epoxide equivalent weights ranging from about 180 to 2000, preferably from about 186 to 1200. Epoxy group-containing acrylic polymers can also be used. These polymers typically have an epoxy equivalent weight ranging from about 750 to 2000.

Examples of polyhydroxyl group-containing materials used to chain extend or increase the molecular weight of the polyepoxide (i.e., through hydroxyl-epoxy reaction) include alcoholic hydroxyl group-containing materials and phenolic hydroxyl group-containing materials. Examples of alcoholic hydroxyl group-containing materials are simple polyols such as neopentyl glycol; polyester polyols such as those described in U.S. Pat. No. 4,148,772; polyether polyols such as those described in U.S. Pat. No. 4,468,307; and urethane diols such as those described in U.S. Pat. No. 4,931,157. Examples of phenolic hydroxyl group-containing materials are polyhydric phenols such as Bisphenol A, phloroglucinol, catechol, and resorcinol. Mixtures of alcoholic hydroxyl group-containing materials and phenolic hydroxyl group-containing materials may also be used. Bisphenol A is preferred.

The active hydrogens associated with the cationic resin include any active hydrogens which are reactive with isocyanates within the temperature range of about 93° to 204° C., preferably about 121° to 177° C. Typically, the active hydrogens are selected from the group consisting of aliphatic hydroxyl and primary and secondary amino, including mixed groups such as hydroxyl and primary amino. Preferably, the cationic resin will have an active hydrogen content of about 1 to 4 milliequivalents, more preferably about 2 to 3 milliequivalents of active hydrogen per gram of resin solids.

The resin contains cationic salt groups, which are preferably incorporated into the resin molecule as follows: The resinous reaction product prepared as described above is further reacted with a cationic salt group former. By "cationic salt group former" is meant a material which is reactive with epoxy groups and which can be acidified before, during, or after reaction with the epoxy groups to form cationic salt groups. Examples of suitable materials include amines such as primary or secondary amines which can be acidified after reaction with the epoxy groups to form amine salt groups, or tertiary amines which can be acidified prior to reaction with the epoxy groups and which after reaction with the epoxy groups form quaternary ammonium salt groups. Examples of other cationic salt group formers are sulfides which can be mixed with acid prior to reaction with the epoxy groups and form ternary sulfonium salt groups upon subsequent reaction with the epoxy groups.

When amines are used as the cationic salt formers, monoamines are preferred, and hydroxyl-containing amines are particularly preferred. Polyamines may be used but are not recommended because of a tendency to gel the resin.

Tertiary and secondary amines are preferred to primary amines because primary amines are polyfunctional with respect to epoxy groups and have a greater tendency to gel the reaction mixture. If polyamines or primary amines are used, they should be used in a substantial stoichiometric excess to the epoxy functionality in the polyepoxide so as to prevent gelation and the excess amine should be removed from the reaction mixture by vacuum stripping or other technique at the end of the reaction. The epoxy may be added to the amine to ensure excess amine.

Examples of hydroxyl-containing amines are alkanolamines, dialkanolamines, trialkanolamines, alkyl alkanolamines, and aralkyl alkanolamines containing from 1 to 18 carbon atoms, preferably 1 to 6 carbon atoms in each of the alkanol, alkyl and aryl groups. Specific examples include ethanolamine, N-methylethanolamine, diethanolamine, N-phenylethanolamine, N,N-dimethylethanolamine, N-methyldiethanolamine, triethanolamine and N-(2-hydroxyethyl)-piperazine.

Amines such as mono, di, and trialkylamines and mixed aryl-alkyl amines which do not contain hydroxyl groups or amines substituted with groups other than hydroxyl which do not negatively affect the reaction between the amine and the epoxy may also be used. Specific examples include ethylamine, methylethylamine, triethylamine, N-benzyldimethylamine, dicocoamine and N,N-dimethylcyclohexylamine.

Mixtures of the above mentioned amines may also be used.

The reaction of a primary and/or secondary amine with the polyepoxide takes place upon mixing of the amine and polyepoxide. The amine may be added to the polyepoxide or vice versa. The reaction can be conducted neat or in the presence of a suitable solvent such as methyl isobutyl ketone, xylene, or 1-methoxy-2-propanol. The reaction is generally exothermic and cooling may be desired. However, heating to a moderate temperature of about 50° to 150° C. may be done to hasten the reaction.

The reaction product of the primary and/or secondary amine and the polyepoxide is made cationic and water dispersible by at least partial neutralization with an acid. Suitable acids include organic and inorganic acids such as formic acid, acetic acid, lactic acid, phosphoric acid and sulfamic acid. By "sulfamic acid" is meant sulfamic acid itself or derivatives thereof; i.e., an acid of the formula: ##STR1## wherein R is hydrogen or an alkyl group having 1 to 4 carbon atoms. Sulfamic acid is preferred. Mixtures of the above mentioned acids may also be used.

The extent of neutralization varies with the particular reaction product involved. However, sufficient acid should be used to disperse the electrodepositable composition in water. Typically, the amount of acid used provides at least 20 percent of all of the total neutralization. Excess acid may also be used beyond the amount required for 100 percent total neutralization.

In the reaction of a tertiary amine with a polyepoxide, the tertiary amine can be prereacted with the neutralizing acid to form the amine salt and then the amine salt reacted with the polyepoxide to form a quaternary salt group-containing resin. The reaction is conducted by mixing the amine salt with the polyepoxide in water. Typically, the water is present in an amount ranging from about 1.75 to about 20 percent by weight based on total reaction mixture solids.

In forming the quaternary ammonium salt group-containing resin, the reaction temperature can be varied from the lowest temperature at which the reaction will proceed, generally room temperature or slightly thereabove, to a maximum temperature of about 100° C. (at atmospheric pressure). At higher pressures, higher reaction temperatures may be used. Preferably, the reaction temperature is in the range of about 60° to 100° C. Solvents such as a sterically hindered ester, ether, or sterically hindered ketone may be used, but their use is not necessary.

In addition to the primary, secondary, and tertiary amines disclosed above, a portion of the amine that is reacted with the polyepoxide can be a ketimine of a polyamine, such as is described in U.S. Pat. No. 4,104,147, column 6, line 23 to column 7, line 23. The ketimine groups decompose upon dispersing the amine-epoxy resin reaction product in water.

In addition to resins containing amine salts and quaternary ammonium salt groups, cationic resins containing ternary sulfonium groups may be used in the composition of the present invention. Examples of these resins and their method of preparation are described in U.S. Pat. Nos. 3,793,278 to DeBona and 3,959,106 to Bosso et al.

The extent of cationic salt group formation should be such that when the resin is mixed with an aqueous medium and other ingredients, a stable dispersion of the electrodepositable composition will form. By "stable dispersion" is meant one that does not settle or is easily redispersible if some settling occurs. Moreover, the dispersion should be of sufficient cationic character that the dispersed resin particles will migrate toward and electrodeposit on a cathode when an electrical potential is set up between an anode and a cathode immersed in the aqueous dispersion.

Generally, the cationic resin in the electrodepositable composition of the present invention contains from about 0.1 to 3.0, preferably from about 0.1 to 0.7 milliequivalents of cationic salt group per gram of resin solids. The cationic resin is preferably non-gelled, having a number average molecular weight ranging from about 2000 to about 15,000, preferably from about 5000 to about 10,000. By "non-gelled" is meant that the resin is substantially free from crosslinking, and prior to cationic salt group formation, the resin has a measurable intrinsic viscosity when dissolved in a suitable solvent. In contrast, a gelled resin, having an essentially infinite molecular weight, would have an intrinsic viscosity too high to measure.

The electrodepositable composition of the present invention also contains a capped polyisocyanate curing agent. The polyisocyanate curing agent may be a fully capped polyisocyanate with substantially no free isocyanate groups, or it may be partially capped and reacted with the resin backbone as described in U.S. Pat. No. 3,984,299. The polyisocyanate can be an aliphatic or an aromatic polyisocyanate or a mixture of the two. Diisocyanates are preferred, although higher polyisocyanates can be used in place of or in combination with diisocyanates.

Examples of suitable aliphatic diisocyanates are straight chain aliphatic diisocyanates such as 1,4-tetramethylene diisocyanate and 1,6-hexamethylene diisocyanate. Also, cycloaliphatic diisocyanates can be employed. Examples include isophorone diisocyanate and 4,4'-methylene-bis-(cyclohexyl isocyanate). Examples of suitable aromatic diisocyanates are p-phenylene diisocyanate, diphenylmethane-4,4'-diisocyanate and 2,4- or 2,6-toluene diisocyanate. Examples of suitable higher polyisocyanates are triphenylmethane-4,4',4"-triisocyanate, 1,2,4-benzene triisocyanate and polymethylene polyphenyl isocyanate.

Isocyanate prepolymers, for example, reaction products of polyisocyanates with polyols such as neopentyl glycol and trimethylol propane or with polymeric polyols such as polycaprolactone diols and triols (NCO/OH equivalent ratio greater than one) can also be used. A mixture of diphenylmethane-4,4'-diisocyanate and polymethylene polyphenyl isocyanate is preferred.

Any suitable aliphatic, cycloaliphatic, or aromatic alkyl monoalcohol may be used as a capping agent for the polyisocyanate in the composition of the present invention including, for example, lower aliphatic alcohols such as methanol, ethanol, and n-butanol; cycloaliphatic alcohols such as cyclohexanol; aromatic-alkyl alcohols such as phenyl carbinol and methylphenyl carbinol. Glycol ethers may also be used as capping agents. Suitable glycol ethers include ethylene glycol butyl ether, diethylene glycol butyl ether, ethylene glycol methyl ether and propylene glycol methyl ether. Diethylene glycol butyl ether is preferred among the glycol ethers.

Other suitable capping agents include oximes such as methyl ethyl ketoxime, acetone oxime and cyclohexanone oxime and lactams such as epsilon-caprolactam.

The polyisocyanate curing agent is usually present in the electrodepositable composition in an amount ranging from about 5 to 60 percent by weight, preferably from about 25 to 50 percent by weight based on total weight of resin solids.

Organotin catalysts are also present in the electrodepositable composition of the present invention, preferably in the form of a dispersion. The catalysts, which are often solids, are typically dispersed in a conventional pigment grinding vehicle such as those disclosed in U.S. Pat. No. 4,007,154, by a grinding or milling process. The catalysts are typically used in amounts of about 0.05 to 1 percent by weight tin based on weight of resin solids. Suitable catalysts include dioctyltin oxide and dibutyltin oxide.

At low organic tin levels in conventional systems, the appearance of the cured coating can be a problem. The presence of the acid functional compound in the electrodepositable composition allows for the use of relatively low levels of organic tin catalyst; i.e., from about 0.05 to 0.5 percent tin by weight based on weight of resin solids, with good cure response and appearance properties.

The acid functional compound added to the electrodepositable composition of the present invention is water immiscible so as to be electrodepositable on the cathode, and has a hydrocarbon chain (excluding carbon atoms associated with the acid functionality; i.e., with the carboxyl group) of at least 5 carbon atoms, preferably from about 5 to about 34 carbon atoms, more preferably from about 9 to about 34 carbon atoms, and most preferably about 15 to 19 carbon atoms.

Preferred acid functional compounds are carboxylic acids. The acid functional compound can be monocarboxylic acid functional or may contain more than one acid functional group. The hydrocarbon chain of the acid functional compound may be aliphatic or aromatic, may be saturated or unsaturated, and may be branched, linear, or cyclic, including polycyclic. The hydrocarbon chain of the acid functional compound may also be substituted. Examples of substituents include hydroxyl groups. Examples of aliphatic saturated carboxylic acids include isodecanoic acid, lauric acid, hexanoic acid, dimer fatty acid, and stearic acid. Examples of aliphatic unsaturated carboxylic acids include oleic acid, 9-11 octadecadienoic acid, 9-12 octadecadienoic acid (linoleic acid), linolenic acid, and mixtures thereof. Examples of substituted carboxylic acids include 12-hydroxy stearic acid.

Suitable polycyclic carboxylic acids useful as the water immiscible acid functional compound with a hydrocarbon chain length of at least 5 carbon atoms include abietic acid, which is preferred as well as natural sources of abietic acid. Natural sources of abietic acid of varying purity include gum rosin, wood rosin, and tall oil rosin. Abietic acid may be used in its natural form or it may be purified using techniques known to those skilled in the art before being added to the electrodepositable composition of the present invention. For example, dihydroabietic acid and dehydroabietic acid can be used in mixtures with each other and with abietic acid. In its natural form as a rosin or rosin acid, the abietic acid may be present with isomeric forms such as levoprimaric and resin acids of the pimaric type having a phenanthrene nucleus. The natural sources can also include the oleoresin material with the presence some or all of the turpentine oils or distillates. Since rosin is a complex mixture of mainly twenty carbon atom fused ring, mono- carboxylic acids and a small amount of nonacidic components, where the resin acid molecule has the double bonds and the carboxylic acid group, any derivative can be used that maintains the carboxylic acid group. For example, hydrogenated derivatives of the oleoresin and rosin can be used. One suitable example of abietic acid containing tall oil that can be used is Unitol NCY partially hydrogenated tall oil from Union Camp, Savannah, Ga.

The acid functional compound may be incorporated into the electrodepositable composition in several ways. It may be added to the final reaction mixture of the main vehicle; i.e., the active hydrogen-containing resin, just before solubilization with water and acid as described above. Alternatively, it may be added to a partially solubilized resin kept at sufficiently high solids so as to be sheared into the final composition. By "partially solubilized" is meant that the resin is fully neutralized with respect to acid functionality, but only partially water-thinned; i.e., diluted. Additionally, it may be co-dispersed with polyepoxide-polyoxyalkylene-polyamine modifying anti-crater resins such as those described in U.S. Pat. No. 4,423,166. It may also be dispersed in a conventional pigment grinding vehicle such as those disclosed in U.S. Pat. No. 4,007,154, by a grinding or milling process, and be a component of a pigment paste.

The acid functional compound is added to and present in the electrodepositable composition in the form of an acid; i.e., it is not formed in situ by the decomposition or hydrolysis of a metal salt or catalyst. The acid functional compound is added to the electrodepositable composition as a compound containing free acid functional groups. Moreover, the acid functional compound is not reacted into the cationic resin backbone; i.e., to form an epoxy ester during the epoxy extension reaction, nor does it serve to any substantial extent to solubilize the main vehicle. Though not intending to be bound by any particular theory, it is believed that because of the immiscibility of the acid functional compounds, they do not protonize well and hence do not solubilize the main vehicle as do the specific acids such as sulfamic acid, lactic acid, etc., mentioned above that are added for the purpose of solubilization of the main vehicle.

The acid functional compound is usually present in the electrodepositable composition in an amount ranging from about 0.1 to 3.0 percent by weight based on weight of main vehicle resin solids; i.e., the active hydrogen-containing cationic resin and capped polyisocyanate curing agent, preferably from about 0.4 to 1.5 percent by weight based on weight of main vehicle resin solids.

The electrodepositable composition may optionally contain a coalescing solvent such as hydrocarbons, alcohols, esters, ethers and ketones. Examples of preferred coalescing solvents are alcohols, including polyols, such as isopropanol, butanol, 2-ethylhexanol, ethylene glycol and propylene glycol; ethers such as the monobutyl and monohexyl ethers of ethylene glycol; and ketones such as methyl isobutyl ketone and isophorone. The coalescing solvent is usually present in an amount up to about 40 percent by weight, preferably ranging from about 0.05 to 25 percent by weight based on total weight of the electrodepositable composition.

The electrodepositable composition of the present invention may further contain pigments and various other optional additives such as plasticizers, surfactants, wetting agents, defoamers, and anti-cratering agents.

Examples of suitable surfactants and wetting agents include alkyl imidazolines such as those available from Geigy Industrial Chemicals as GEIGY AMINE C, and acetylenic alcohols available from Air Products and Chemicals as SURFYNOL. Examples of defoamers include a hydrocarbon containing inert diatomaceous earth available from Crucible Materials Corp. as FOAMKILL 63. Examples of anti-cratering agents are polyepoxide-polyoxyalkylene-polyamine reaction products such as those described in U.S. Pat. No. 4,423,166. These optional ingredients, when present, are usually used in an amount up to 30 percent by weight, typically about 1 to 20 percent by weight based on weight of resin solids.

Suitable pigments include, for example, iron oxides, lead oxides, strontium chromate, carbon black, coal dust, titanium dioxide, talc, clay, silica, lead silicate, and barium sulfate, as well as color pigments such as cadmium yellow, cadmium red, chromium yellow, and the like. The pigment content of the aqueous dispersion, generally expressed as the pigment to resin (or pigment to binder) ratio (P/B) is usually about 0.05:1 to 1:1.

The composition of the present invention comprising the cationic resin, the capped polyisocyanate curing agent, the catalyst, the acid functional compound, and the optional additives mentioned above is used in an electrodeposition process in the form of an aqueous dispersion. By "dispersion" is meant a two-phase transparent, translucent, or opaque aqueous resinous system in which the resin, pigment, and water insoluble materials are in the dispersed phase while water and water soluble materials comprise the continuous phase. The dispersed phase has an average particle size less than about 10 microns, preferably less than 5 microns. The aqueous dispersion preferably contains at least about 0.05 and usually about 0.05 to 50 percent by weight resin solids, depending on the particular end use of the dispersion.

Addition of the acid functional compound to the electrodepositable composition of the present invention improves the cure response of the composition when it is used in an electrocoating process. By this is meant that the temperature range for curing of the electrodepositable composition of the present invention may be about 310° to 325° F. (154.5° to 162.7° C.), as opposed to 325° to 340° F. (162.7° to 171.1° C.) for conventional electrodepositable compositions at conventional organotin catalyst levels; i.e., about 0.5 to 1.0 percent by weight tin based on weight of resin solids. The composition of the present invention also demonstrates improved cure response as measured by solvent resistance when cured at underbake temperatures (about 310° F., 154.5° C.) compared to conventional electrodepositable compositions without the acid functional compound, once again at optimized organotin catalyst levels. Moreover, the cure rate is improved; i.e., at a given temperature, a deposited film of the present invention cures more quickly than a comparable film without the acid functional compound, as measured by rate of weight loss of a deposited film during baking. Alternatively, the amount of organotin catalyst can be reduced while maintaining cure at normal temperatures.

Addition of the acid functional compound to the electrodepositable composition of the present invention also improves the appearance of the composition when it is used in an electrocoating process. Cationic electrodeposition compositions are conventionally formulated with lead as either a pigment or a soluble lead salt. When these compositions also contain low levels of organotin catalysts; i.e., about 0.05 to 0.5 percent by weight tin based on weight of total resin solids, the cured deposited films exhibit a "fuzzy" or bristle-like appearance, particularly with aging of the electrodeposition bath. Addition of the acid functional compound to the electrodepositable composition in accordance with the present invention improves the appearance of cured electrodeposited films, eliminating the fuzzy appearance even with low levels of organotin catalyst in the composition.

Addition of the preferred acid functional compound, abietic acid, to the electrodepositable composition likewise improves cure and appearance, while maintaining the humidity and salt solution resistance of the composition when it is used as a coating over electrogalvanized substrate.

In the process of electrodeposition the aqueous dispersion is placed in contact with an electrically conductive anode and cathode. Upon passage of an electric current between the anode and cathode while they are in contact with the aqueous dispersion, an adherent film of the electrodepositable composition will deposit in a substantially continuous manner on the cathode. The film will contain the active hydrogen-containing resin, the capped polyisocyanate curing agent, the tin catalyst, the acid functional compound, and the optional additives from the non-aqueous phase of the dispersion. Electrodeposition is usually carried out at a constant voltage in the range of from about 1 volt to several thousand volts, typically between 50 and 500 volts. Current density is usually between about 1.0 ampere and 15 amperes per square foot (10.8 to 161.5 amperes per square meter) and tends to decrease quickly during the electrodeposition process, indicating formation of a continuous self-insulating film. Any electroconductive substrate, especially metal substrates such as steel, zinc, aluminum, copper, magnesium or the like can be coated with the electrodepositable composition of the present invention. Steel substrates are preferred. It is customary to pretreat the substrate with a phosphate conversion, usually a zinc phosphate conversion coating, followed by a rinse which seals the conversion coating.

After deposition, the coating is heated to cure the deposited composition. The heating or curing operation is usually carried out at a temperature in the range of from 250° to 400° F. (121.1° to 204.4° C.), preferably from 300° to 340° F. (148.8° to 171.1° C.) for a period of time ranging from 10 to 60 minutes. The thickness of the resultant film is usually from about 10 to 50 microns.

The invention will be further described by reference to the following examples. Unless otherwise indicated, all parts and percentages are by weight.

EXAMPLE I

Examples I-A to I-O illustrate the effect of adding various water immiscible acid functional compounds to a cationic electrodepositable composition in accordance with the present invention, compared to the effect of various non-acid functional compounds added to a cationic electrodepositable composition.

EXAMPLE I-A (Control)

This example describes the preparation of a cationic electrodeposition bath containing no additive. A main vehicle (i.e., the active hydrogen-containing cationic resin and capped polyisocyanate curing agent) was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by Weight                                              ______________________________________                                         EPON 828.sup.1    614.68                                                       Bisphenol A-ethylene oxide                                                                       250.00                                                       adduct                                                                         (1:6 molar ratio)                                                              Bisphenol A       265.42                                                       Methyl isobutyl ketone                                                                           59.48                                                        Ethyltriphenyl phosphonium                                                                       0.6                                                          iodide                                                                         Crosslinker.sup.2 682.85                                                       Diketimine.sup.3  56.01                                                        N-methyl ethanolamine                                                                            48.68                                                        ______________________________________                                          .sup.1 Polyglycidyl ether of Bisphenol A, available from Shell Oil and         Chemical Co.                                                                   .sup.2 The capped polyisocyanate crosslinker was prepared from the             following mixture of ingredients:                                        

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         Polyisocyanate.sup.a                                                                             1325.00                                                      Methyl isobutyl ketone                                                                           221.81                                                       (MIBK)                                                                         2-(2-Butoxyethoxy)ethanol                                                                        162.23                                                       Dibutyltin dilaurate (DBTDL)                                                                     0.2                                                          2-Butoxy ethanol  1063.62                                                      ______________________________________                                          .sup.a Mixture of diphenyl4,4diisocyanate and polyphenyl polyisocyanate,       available from Miles, Inc. as MONDUR MR.                                       The polyisocyanate, MIBK, and DBTDL were charged to a reaction flask unde      a nitrogen atmosphere. 2(2-Butoxyethoxy)ethanol was added slowly allowing      the reaction mixture to exotherm to a temperature between 45 and               50° C. Upon completion of the addition the reaction mixture was         held at 50° C. for 30 minutes.                                          2Butoxy ethanol was then added and the mixture allowed to exotherm to          110° C. and held there until infrared analysis indicated complete       consumption of the isocyanate.                                                 .sup.3 Diketimine derived from diethylene triamine and methyl isobutyl         ketone (MIBK) (73% solids in MIBK)                                       

A reaction vessel was charged with the EPON 828, Bisphenol A-ethylene oxide adduct, Bisphenol A and MIBK. This mixture was heated under a nitrogen blanket to 125° C. Ethyl triphenylphosphonium iodide was then added and the reaction mixture allowed to exotherm to a temperature of about 145° C. The reaction was held at 145° C. for two hours and the epoxy equivalent weight was determined. At this point, the crosslinker, the diketimine, and N-methyl ethanolamine were added in succession. The reaction mixture exothermed and then a temperature of 132° C. was established and maintained for an hour. The resin mixture (1684 parts) was dispersed in aqueous medium by adding it to a mixture of 38.34 parts sulfamic acid and 1220.99 parts deionized water. The dispersion was further thinned with 657.63 parts deionized water and 666.28 parts deionized water in stages and vacuum stripped to remove organic solvent to yield a dispersion having a solids content of 41.2 percent and a particle size of 984 Angstroms.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by Weight                                              ______________________________________                                         Main vehicle prepared above                                                                      1395.8                                                       Co-resin 1.sup.1  168.2                                                        Butyl CARBITOL formal                                                                            27.1                                                         plasticizer.sup.2                                                              Co-resin 2.sup.3  73.9                                                         Deionized water   1943.7                                                       E-6066 paste.sup.4                                                                               191.3                                                        ______________________________________                                          .sup.1 An aqueous dispersion of a flexibilizerflow control agent generall      in accordance with U.S. Pat. No. 4,423,166 was prepared for use with the       electrodepositable composition. The flexibilizerflow control agent was         prepared from a polyepoxide (EPON 828) and a polyoxyalkylenepolyamine          (JEFFAMINE D2000 from Texaco Chemical Co.). The flexibilizerflow control       agent was dispersed in aqueous medium with the aid of lactic acid and the      dispersion had a resin solids content of 36.2%.                                .sup.2 The reaction product of 2 moles of diethylene glycol butyl ether        and 1 mole of formaldehyde, prepared as generally described in U.S. Pat.       No. 4,891,111.                                                                 .sup.3 A cationic microgel prepared as generally described in Examples A       and B of U.S. Pat. No. 5,096,556, with the exception that acetic acid          instead of lactic acid was used to disperse the soap of Example A,             ethylene glycol butyl ether instead of MIBK was used as a solvent in the       soap of Example A, and EPON 828 solution was added after stripping rather      than before in Example B. The resin had a final solids content of 18.3%.       .sup.4 A pigment paste commercially available from PPG Industries Inc.,        containing 27.2% titanium dioxide, 1.4% carbon black, 15.9% aluminum           silicate, 5.7% basic lead silicate, and 3.8% dibutyltin oxide.           

EXAMPLES I-B to I-O

Main vehicles and electrodeposition baths were prepared as generally described in Example I-A; however, various water immiscible acid functional compounds or non-acid functional compounds as reported in Table I below were added to the cationic main vehicle reaction mixture at 1% on main vehicle resin solids after the exotherm and one-hour hold at 132° C. described in the main vehicle preparation method above.

The baths for the above examples including the control were ultrafiltered, removing 20% of the total weight of the bath as ultrafiltrate and replacing the ultrafiltrate with deionized water. Zinc phosphate pretreated steel panels were immersed in the baths and electrocoated with the electrodepositable compositions at 275 volts for 2 min. at a bath temperature of 87°-95° F. (30.5°-35° C.). After rinsing with deionized water, the panels were baked for 30 minutes at. 310° F. (154.5° C.), 325° F. (162.7° C.), or 340° F. (171.1° C.). Resulting film builds were about 0.9 mils (22.9 microns). The cured coatings were evaluated for appearance as measured by the surface profile (R_(A)) described below and for cure response as measured by acetone resistance and cure rate (TGA). The results are reported in Table I below.

                  TABLE I                                                          ______________________________________                                                                        Acetone                                         Example    Additive     R.sub.A.sup.1                                                                         Resistance.sup.2                                                                       TGA.sup.3                               ______________________________________                                         I-A (Control)                                                                             none         14.5    20     22                                      I-B        oleic acid   8.3    >100    77                                      I-C        9-11,9-12    7.3    >100    49                                                 octadecadienoic                                                                acid                                                                I-D        stearic acid 6.9    >100    88                                      I-E        linoleic acid                                                                               6.8    >100    64                                      I-F        linolenic acid                                                                              7.7    >100    88                                      I-G        12-hydroxy stearic                                                                          9.3    >100    36                                                 acid                                                                I-H        lauric acid  11.5   >100    102                                     I-I        isodecanoic acid                                                                            9.8    >100    66                                      I-J        hexanoic acid                                                                               12.1   >100    83                                      I-K        isovaleric acid                                                                             18.4   >100    57                                      I-L        dimer fatty acid                                                                            8.2    >100    60                                      I-M (Comparative)                                                                         oleyl amine  6.7     13     35                                      I-N (Comparative)                                                                         oleyl alcohol                                                                               9.8     45     43                                      I-O (Comparative)                                                                         squalene     9.8     55     38                                      ______________________________________                                          .sup.1 Data obtained from panels coated in baths aged two (2) weeks.           Relative roughness of the coating surface is measured with a Surfanalyzer      Model 219010-01, Federal products, Inc. The number reported is the averag      roughness, or the average vertical distance of any point on the surface        from a centerline determined by a stylus moving across the surface,            expressed in microinches. Lower numbers indicate greater smoothness. Thes      data were obtained from panels cured for 30 minutes at 340° F.          (171.1° C.).                                                            .sup.2 An acetone saturated cloth was firmly rubbed back and forth across      the cured coating surface. The number reported is the number of double         rubs required to expose the metal surface. These data were obtained from       panels cured for 30 minutes at 310° F. (154.5° C.).              .sup.3 ThermoGravimetric Analysis: he weight loss of a curing coating is       monitored versus time for thirty (30) minutes at 325° F.                (162.7° C.). The linear portion of the plot of the rate of change       of the rate of weight loss versus time is recorded, expressed as percent       weight loss per minute.sup.2 times 10.sup.3 (% weight loss/min.sup.2           × 10.sup.3). The higher the values, the faster the weight loss and       the greater the cure rate.                                               

The data in Table I indicate that all the acid-functional compounds tested tend to improve cure, while other long-chain materials and highly unsaturated materials do not significantly improve cure. As the total number of carbons in the hydrocarbon chain of the acid-functional compound increases, the appearance of the cured coating tends to improve.

EXAMPLE II

The following examples (II-A to II-C) illustrate the effect of adding various levels of a water immiscible acid functional compound to a cationic electrodepositable composition in accordance with the present invention. The electrodeposition baths were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I. Results are reported in Table II below.

                  TABLE II                                                         ______________________________________                                                                        Acetone                                         Example  Additive Amount.sup.1                                                                       R.sub.A  Resistance                                                                            TGA                                      ______________________________________                                         I-A (Control)                                                                           none         14.5      20    22                                       II-A     0.5% oleic acid                                                                             9.2      >100   52                                       I-B      1.0% oleic acid                                                                             8.3      >100   77                                       II-B     2.0% oleic acid                                                                             8.6      >100   113                                      II-C     3.0% oleic acid                                                                             9.2      >100   185                                      ______________________________________                                          .sup.1 Amount reported is percent by weight based on main vehicle solids.

The data in Table II indicate that the effect of an acid functional compound on cure rate (TGA) is proportional to its level.

EXAMPLE III

The following examples (III-A and III-B) illustrate the effect of adding a water immiscible acid functional compound to a cationic electrodepositable composition containing a polyisocyanate crosslinking agent capped with a "sluggish" capping agent; i.e., a capping agent such as a secondary alcohol which does not readily uncap at standard cure temperatures. The compositions were prepared as in Example I, with the following exception. The capped polyisocyanate crosslinker was prepared from the following mixture of ingredients:

    ______________________________________                                         Ingredients     Parts by Weight                                                ______________________________________                                         Polyisocyanate.sup.a                                                                           1325.00                                                        MIBK            193.39                                                         Monomethyl ether of                                                                            901.2                                                          propylene glycol                                                               DBTDL           0.2                                                            ______________________________________                                          .sup.a MONDUR MR.                                                        

The polyisocyanate, MIBK, and DBTDL were charged to a reaction flask under a nitrogen atmosphere. The monomethyl ether of propylene glycol was added slowly allowing the reaction mixture to exotherm to a temperature between 100° and 110° C. Upon completion of the addition the reaction mixture was held at 110° C. until infrared analysis indicated complete consumption of the isocyanate.

The crosslinker was incorporated into the electrodeposition bath as in Example I-A, except at 31% solids on solids instead of at 34% solids on solids.

The electrodepositable composition of Example III-A contained no acid functional materials, while that of Example III-B contained 1% oleic acid by weight, based on weight of main vehicle resin solids. The electrodeposition baths were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I unless otherwise indicated. Results are reported in Table III below.

                  TABLE III                                                        ______________________________________                                                               Acetone                                                                               Acetone                                                  Additive       Resistance                                                                            Resistance                                                                            TGA.sup.3                                                                            TGA.sup.4                            Example                                                                               Amount   R.sub.A                                                                              310° F..sup.1                                                                  340° F..sup.2                                                                  325° F.                                                                       340° F.                       ______________________________________                                         III-A  none     6.7    1      45    28     55                                  (control)                                                                      III-B  1.0%     6.1   95     >100   38    125                                  ______________________________________                                          .sup.1 These data were obtained from coated panels cured for 30 minutes a      310° F. (154.5° C.).                                             .sup.2 These data were obtained from coated panels cured for 30 minutes a      340° F. (171.1° C.).                                             .sup.3 These data were obtained from coated panels cured for 30 minutes a      325° F. (162.7° C.).                                             .sup.4 These data were obtained from coated panels cured for 30 minutes a      340° F. (171.1° C.).                                       

The data in Table III indicate that acid functional compounds improve the cure rate (TGA) in a system containing a polyisocyanate crosslinking agent capped with a "sluggish" capping agent. Acetone resistance and appearance are also improved.

EXAMPLE IV

The following examples (IV-A and IV-B) illustrate the effect of adding water immiscible acid functional compound to a cationic electrodepositable composition containing dioctyltin oxide instead of dibutyltin oxide, at equal tin levels, as the catalyst.

EXAMPLE IV-A

This example demonstrates the preparation of a cationic electrodepositable composition containing dioctyltin oxide catalyst and no acid functional compound.

A pigment paste was prepared from the following ingredients:

    ______________________________________                                         Ingredients      Parts by Weight                                               ______________________________________                                         Pigment grinding vehicle.sup.1                                                                  338.0                                                         Deionized water  507.1                                                         Titanium dioxide.sup.2                                                                          564.0                                                         Aluminum silicate.sup.3                                                                         330.0                                                         Carbon Black.sup.4                                                                              28.0                                                          Basic lead silicate.sup.5                                                                       118.0                                                         Dioctyltin oxide 114.9                                                         ______________________________________                                          .sup.1 The pigment grinding vehicle was prepared by first preparing a          quaternizing agent followed by reacting the quaternizing agent with an         epoxy resin. The quaternizing agent was prepared as follows:             

    ______________________________________                                                           Solution   Solid                                             Ingredients       weight (grams)                                                                            weight                                            ______________________________________                                         2-Ethylhexanol half-capped                                                                       320        304                                               toluene diisocyanate in                                                        MIBK                                                                           Dimethylethanolamine                                                                             87.2       87.2                                              (DMEA)                                                                         Aqueous lactic acid                                                                              117.6      58.2                                              solution                                                                       2-Butoxyethanol   39.2       --                                                ______________________________________                                    

The 2-ethylhexanol half-capped toluene diisocyanate was added to the DMEA in a suitable reaction vessel at room temperature. The mixture exothermed and was stirred for one hour at 80° C. The aqueous lactic acid solution was then charged followed by the addition of 2-butoxyethanol. The reaction mixture was stirred for about one hour at 65° C. to form the quaternizing agent.

The pigment grinding vehicle was prepared as follows:

    ______________________________________                                                            Solution   Solid                                            Ingredients        weight (grams)                                                                            weight                                           ______________________________________                                         EPON 829.sup.a     710        682                                              Bisphenol A        289.6      289.6                                            2-Ethylhexanol half-capped                                                                        406        386.1                                            toluene diisocyanate in MIBK                                                   Quaternizing agent described                                                                      496.3      421.9                                            above                                                                          Deionized water    71.2       --                                               2-Butoxyethanol    1490       --                                               ______________________________________                                          .sup.a Diglycidyl ether of Bisphenol A available from Shell Oil and            Chemical Co.                                                                   The EPON 829 and Bisphenol A were charged under a nitrogen atmosphere to       suitable reactor and heated to 150 to 160° C. to initiate an            exotherm. The reaction mixture was permitted to exotherm for one hour at       150 to 160° C. The reaction mixture was then cooled to 120°      C. and the 2ethylhexanol halfcapped toluene diisocyanate added. The            temperature of the reaction mixture was held at 110 to 120° C. for      one hour followed by the addition of the 2butoxyethanol. The reaction          mixture was then cooled to 85 to 90° C., homogenized and charged        with water followed by the quaternizing agent. The temperature of the          reaction mixture was held at 80 to 85° C. until an acid value of        about 1 was obtained. The final product had a solids content of about          57.1%.                                                                         .sup.2 Available from E. I. Du Pont de Nemours and Co. as R900.                .sup.3 Available from Engelhard Corp. as ASP200.                               .sup.4 Available from the Columbian division of Cities Service Co. as          Raven 410.                                                                     .sup.5 Available from EaglePicher Industries, Inc. as EP202.             

The pigment paste was sand milled to a Hegman reading of 7.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example I-A                                                                       1456.5                                                      Co-resin 1 of Example I-A                                                                         178.0                                                       Butyl CARBITOL formal                                                                             28.2                                                        plasticizer                                                                    Co-resin 2 of Example I-A                                                                         77.6                                                        Deionized water    1865.6                                                      Pigment paste described above                                                                     194.1                                                       ______________________________________                                    

EXAMPLE IV-B

This example demonstrates the preparation of a cationic electrodepositable composition containing dioctyltin oxide catalyst and a water immiscible acid functional compound at 1 weight percent on main vehicle solids.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example I-A                                                                       971.0                                                       Main vehicle of Example II-C                                                                      454.2                                                       Co-resin 1 of Example I-A                                                                         178.0                                                       Butyl CARBITOL formal                                                                             28.2                                                        plasticizer                                                                    Co-resin 2 of Example I-A                                                                         77.6                                                        Deionized water    1896.9                                                      Pigment paste of Example IV-A                                                                     194.1                                                       ______________________________________                                    

The electrodeposition baths of Examples IV-A and IV-B were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I. Results are reported in Table IV below.

                  TABLE IV                                                         ______________________________________                                         Example  Additive Amount                                                                            R.sub.A                                                                               Acetone Resistance                                                                        TGA                                     ______________________________________                                         IV-A (Control)                                                                          none        9.8    >100        56                                                                 (coating softened)                                 IV-B     1.0% oleic acid                                                                            9.7    >100       147                                                                 (no softening)                                     ______________________________________                                    

The data in Table IV indicate that addition of a water immiscible acid functional compound to a cationic electrodepositable composition containing dioctyltin oxide clearly improves the cure rate, as shown by the marked increase in TGA.

EXAMPLE V

The following examples (V-A and V-B) illustrate the effect of reacting a water immiscible acid functional compound into the main vehicle at 1% on main vehicle solids, forming an epoxy ester, compared to post-adding the acid functional compound to the cationic electrodepositable composition.

EXAMPLE V-A

This example describes the preparation of a cationic electrodeposition bath containing 1% oleic acid on main vehicle solids, post-added to the fully reacted resin. A main vehicle was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by Weight                                              ______________________________________                                         EPON 828          1844.03                                                      Bisphenol A-ethylene oxide                                                                       75.00                                                        adduct (1:6 molar ratio)                                                       Bisphenol A       796.27                                                       Methyl isobutyl ketone                                                                           69.19                                                        Ethyltriphenyl phosphonium                                                                       1.80                                                         iodide                                                                         Bisphenol A-ethylene oxide                                                                       675.00                                                       adduct (1:6 molar ratio)                                                       Methyl isobutyl ketone                                                                           10.98                                                        Crosslinker of Example I-A                                                                       2049.23                                                      Diketimine of Example I-A                                                                        168.02                                                       N-methyl ethanolamine                                                                            146.03                                                       ______________________________________                                    

A reaction vessel was charged with the EPON 828, the initial charge of Bisphenol A-ethylene oxide adduct, Bisphenol A and the initial charge of MIBK. This mixture was heated under a nitrogen blanket to 125° C. Ethyl triphenylphosphonium iodide was then added and the reaction mixture allowed to exotherm to a temperature of about 145° C. The reaction was held at 145° C. for two hours and the second charge of Bisphenol A-ethylene oxide adduct was added and the epoxy equivalent weight was determined. At this point, the second charge of MIBK, the crosslinker, the diketimine, and N-methyl ethanolamine were added in succession. The reaction mixture exothermed and then a temperature of 132° C. was established and maintained for an hour. The resin mixture (1500 parts) was dispersed in aqueous medium by adding it to a mixture of 34.72 parts sulfamic acid and 1145.23 parts deionized water. After five minutes 14.25 parts oleic acid was added to the high solids dispersion and further mixed for 30 minutes. The dispersion was further thinned with 581.29 parts deionized water and 603.38 parts deionized water in stages and vacuum stripped to remove organic solvent to yield a dispersion having a solids content of 42.6 percent and a particle size of 861 Angstroms.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by Weight                                              ______________________________________                                         Main vehicle prepared above                                                                      1349.9                                                       Co-resin 1 of Example I-A                                                                        168.2                                                        Butyl CARBITOL formal                                                                            27.1                                                         plasticizer                                                                    Co-resin 2 of Example I-A                                                                        73.9                                                         Deionized water   1989.6                                                       E-6066 paste      191.3                                                        ______________________________________                                    

EXAMPLE V-B

This example describes the preparation of a cationic electrodeposition bath containing 1% oleic acid on main vehicle solids, reacted into the resin during the epoxy extension stage. A main vehicle was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by Weight                                              ______________________________________                                         EPON 828          614.68                                                       Bisphenol A-ethylene oxide                                                                       250.00                                                       adduct (1:6 molar ratio)                                                       Bisphenol A       265.42                                                       Methyl isobutyl ketone                                                                           60.45                                                        Ethyltriphenyl phosphonium                                                                       0.6                                                          iodide                                                                         Oleic acid        18.48                                                        Crosslinker of Example I-A                                                                       683.08                                                       Diketimine to Example I-A                                                                        56.56                                                        N-methyl ethanolamine                                                                            48.68                                                        ______________________________________                                    

A reaction vessel was charged with the EPON 828, Bisphenol A-ethylene oxide adduct, Bisphenol A, oleic acid, and the MIBK. This mixture was heated under a nitrogen blanket to 125° C. Ethyl triphenylphosphonium iodide was then added and the reaction mixture allowed to exotherm to a temperature of about 145° C. The reaction was held at 145° C. for two hours and the epoxy equivalent weight was determined. At this point, the crosslinker, the diketimine, and N-methyl ethanolamine were added in succession. The reaction mixture exothermed and then a temperature of 132° C. was established and maintained for an hour. The resin mixture (1700 parts) was dispersed in aqueous medium by adding it to a mixture of 38.31 parts sulfamic acid and 1219.38 parts deionized water. The dispersion was further thinned with 657.26 parts deionized water and 665.91 parts deionized water in stages and vacuum stripped to remove organic solvent to yield a dispersion having a solids content of 43.1 percent and a particle size of 870 Angstroms.

A cationic electrodeposition bath was prepared as in Example V-A except that the main vehicle of Example V-B was used in place of the main vehicle of Example V-A.

The electrodeposition baths of Examples V-A and V-B were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I. Results are reported in Table V below.

                  TABLE V                                                          ______________________________________                                                                        Acetone                                         Example   Additive Amount                                                                            R.sub.A  Resistance                                                                            TGA                                      ______________________________________                                         V-A       1.0% oleic acid                                                                            9.0      >100   77                                                 (post-add)                                                           V-B       1.0% oleic acid                                                                            10.6      30    25                                                 (reacted in)                                                         ______________________________________                                    

The data in Table V indicate that post-addition of a water immiscible acid functional compound to the cationic electrodepositable composition of Example V provides better appearance, cure, and cure rate than does reaction of the cationic resin with the water immiscible acid functional compound.

EXAMPLE VI

The following examples (VI-A to VI-G) illustrate the effect of adding a water immiscible acid functional compound to the cationic electrodepositable composition with respect to the levels of tin catalyst required for appearance and cure.

EXAMPLE VI-A

This example describes the preparation of a cationic electrodeposition bath containing 1.45% dibutyltin oxide (DBTO) on total resin solids (0.69% tin on total resin solids), and no water immiscible acid functional compound.

A pigment paste was prepared from the following ingredients:

    ______________________________________                                         Ingredients      Parts by Weight                                               ______________________________________                                         Pigment grinding vehicle of                                                                     1515.5                                                        Example IV-A                                                                   Deionized water  2659.0                                                        Titanium dioxide 2712.5                                                        Aluminum silicate                                                                               1582.5                                                        Carbon Black     134.5                                                         Basic lead silicate                                                                             570.5                                                         ______________________________________                                    

The paste was sand milled to a Hegman reading of 7.

A catalyst paste was prepared from the following ingredients:

    ______________________________________                                         Ingredients      Parts by Weight                                               ______________________________________                                         Pigment grinding vehicle                                                                        137.9                                                         of Example IV-A                                                                Dibutyltin oxide 200                                                           Deionized water  268.2                                                         ______________________________________                                    

The paste was sand milled to a Hegman reading of 7.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example I-A                                                                       1391.1                                                      Co-resin 1 of Example I-A                                                                         168.2                                                       Butyl CARBITOL formal                                                                             27.1                                                        plasticizer                                                                    Co-resin 2 of Example I-A                                                                         73.9                                                        Deionized water    1934.7                                                      Pigment paste described above                                                                     172.4                                                       Catalyst paste described above                                                                    32.6                                                        ______________________________________                                    

EXAMPLE VI-B

This example describes the preparation of a cationic electrodeposition bath containing 1.45% DBTO on total resin solids (0.69% tin on total resin solids), and 1% water immiscible acid functional compound on main vehicle solids.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example V-A                                                                       5379.5                                                      Co-resin 1 of Example I-A                                                                         670.3                                                       Butyl CARBITOL formal                                                                             107.8                                                       plasticizer                                                                    Co-resin 2 of Example I-A                                                                         294.7                                                       Deionized water    7928.0                                                      Pigment paste of Example VI-A                                                                     689.5                                                       Catalyst paste of Example VI-A                                                                    130.2                                                       ______________________________________                                    

EXAMPLE VI-C to VI-G

These examples describe the preparation of various cationic electrodeposition baths containing reduced levels of DBTO and 1% acid functional compound on main vehicle solids. The baths were prepared by diluting the bath of Example VI-B, containing 1.45% DBTO on total resin solids, with a bath containing no DBTO, prepared from the following ingredients:

    ______________________________________                                         Ingredients         Parts by Weight                                            ______________________________________                                         Main vehicle of Example V-A                                                                        4049.8                                                     Co-resin 1 of Example I-A                                                                          504.6                                                      Butyl CARBITOL formal plasticizer                                                                  81.2                                                       Co-resin 2 of Example I-A                                                                          221.8                                                      Deionized water     5970.2                                                     Pigment paste of Example VI-A                                                                      572.4                                                      ______________________________________                                    

    ______________________________________                                                Parts by weight          % DBTO (tin) on                                       (Bath of    Parts by weight                                                                             total resin                                    Example                                                                               Example VI-B)                                                                              (DBTO-free Bath)                                                                            solids                                         ______________________________________                                         VI-C   2830.0      970.0        1.08 (0.515)                                   VI-D   2359.0      1441.0       0.9 (0.429)                                    VI-E   1835.0      1965.0       0.7 (0.334)                                    VI-F   1310.0      2490.0       0.5 (0.238)                                    VI-G   786.0       3014.0       0.3 (0.143)                                    ______________________________________                                    

The electrodeposition baths of Examples VI-A to VI-G were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I. Results are reported in Table VI below.

                  TABLE VI                                                         ______________________________________                                                Additive % DBTO                                                                Amount   (tin) on                                                              (oleic   total resin    Acetone                                         Example                                                                               acid)    solids    R.sub.A                                                                             Resistance                                                                               TGA                                   ______________________________________                                         VI-A   0        1.45 (0.691)                                                                             10.7 >100      32                                                                   (extremely soft)                                VI-B   1.0%     1.45 (0.691)                                                                             6.8  >100 (very                                                                               170                                                                  slightly soft)                                  VI-C   1.0%     1.08 (0.515)                                                                             7.7  >100 (soft)                                                                              122                                   VI-D   1.0%     0.9 (0.429)                                                                              7.4  >100      82                                                                   (very soft)                                     VI-E   1.0%     0.7 (0.334)                                                                              8.6  >100      63                                                                   (extremely soft)                                VI-F   1.0%     0.5 (0.238)                                                                              9.8  75        43                                    VI-G   1.0%     0.3 (0.143)                                                                              9.4  40        27                                    ______________________________________                                    

The data in Table VI indicate that the appearance of a coating is improved when the composition contains a water immiscible acid functional compound, for all levels of catalyst tested. Cure, as measured by acetone resistance, is equal for the composition containing 0.7% DBTO with a water immiscible acid functional compound and the composition containing 1.45% DBTO with no acid functional compound. Cure rate as measured by TGA is slightly better for a composition containing 0.5% DBTO with a water immiscible acid functional compound than the composition containing 1.45% DBTO with no water immiscible acid functional compound.

EXAMPLE VII

The following examples (VII-A and VII-B) illustrate the effect of adding a water immiscible acid functional compound to a lead-free cationic electrodepositable primer composition.

EXAMPLE VII-A

This example describes the preparation of a cationic electrodeposition primer bath containing no lead and no water immiscible acid functional compound.

A pigment paste was prepared from the following ingredients:

    ______________________________________                                         Ingredients      Parts by Weight                                               ______________________________________                                         Pigment grinding vehicle of                                                                     1167.8                                                        Example IV-A                                                                   Deionized water  2011.8                                                        Aluminum silicate                                                                               2449.6                                                        Carbon Black     1428.8                                                        Titanium dioxide 121.6                                                         ______________________________________                                    

The pigment paste was sand milled to a Hegman reading of 7.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example I-A                                                                       1462.5                                                      Co-resin 1 of Example I-A                                                                         178.7                                                       Butyl CARBITOL formal                                                                             28.4                                                        plasticizer                                                                    Co-resin 2 of Example I-A                                                                         77.1                                                        Deionized water    1857.7                                                      Pigment paste described above                                                                     195.6                                                       Catalyst paste of Example IV-A                                                                    23.8                                                        ______________________________________                                    

EXAMPLE VII-B

This example describes the preparation of a cationic electrodeposition primer bath containing no lead and 1% water immiscible acid functional compound on main vehicle solids.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by Weight                                             ______________________________________                                         Main vehicle of Example V-A                                                                       1414.3                                                      Co-resin 1 of Example I-A                                                                         178.7                                                       Butyl CARBITOL formal                                                                             28.4                                                        plasticizer                                                                    Co-resin 2 of Example I-A                                                                         77.1                                                        Deionized water    1905.9                                                      Pigment paste of Example VII-A                                                                    195.6                                                       Catalyst paste of Example IV-A                                                                    23.8                                                        ______________________________________                                    

The electrodeposition baths of Examples VII-A and VII-B were prepared and zinc phosphate pretreated steel panels were coated and cured as in Example I. Results are reported in Table VII below.

                  TABLE VII                                                        ______________________________________                                                Additive         Acetone  TGA.sup.3                                                                            TGA.sup.4                               Example                                                                               Amount    R.sub.A.sup.1                                                                         Resistance.sup.2                                                                        325° F.                                                                       340° F.                          ______________________________________                                         VII-A  none      5.61     5       13    48                                     (control)                                                                      VII-B  1.0%      8.45   >100     119   315                                     ______________________________________                                          .sup.1 These data were obtained from coated panels cured for 30 minutes a      340° F. (171.1° C.).                                             .sup.2 These data were obtained from coated panels cured for 30 minutes a      310° F. (154.5° C.).                                             .sup.3 These data were obtained from coated panels cured for 30 minutes a      325° F. (162.7° C.).                                             .sup.4 These data were obtained from coated panels cured for 30 minutes a      340° F. (171.1° C.).                                       

The data in Table VII indicate that addition of water immiscible acid functional compounds to lead-free electrodepositable compositions improve the cure as measured by acetone resistance and TGA, despite the absence of lead as an auxiliary isocyanate decapping catalyst.

EXAMPLE VIII

This example illustrates gum rosin or natural abietic acid as the water immiscible acid functional compound having a hydrocarbon chain of at least 5 carbon atoms. The gun rosin has several unexpected advantages over oleic acid, and that 0.3% abietic acid on main vehicle solids is similar or improved over 0.5% oleic acid on main vehicle solids in all properties.

EXAMPLE VIII-A

This example describes the preparation of a cationic electrodeposition bath containing no additives.

A main vehicle was prepared from the following ingredients.

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         EPON 828          2415.68                                                      Bisphenol A-ethylene oxide                                                                       98.25                                                        adduct (1/6 molar ratio)                                                       Bisphenol A       1043.11                                                      Methyl isobutyl ketone                                                                           90.63                                                        Ethyltriphenyl phosphonium                                                                       2.36                                                         iodide                                                                         Bisphenol A-ethylene oxide                                                                       884.25                                                       adduct (1/6 molar ratio)                                                       Methyl isobutyl ketone                                                                           328.31                                                       Crosslinker.sup.1 2736.09                                                      Diketimine.sup.2  224.04                                                       N-methyl ethanol amine                                                                           191.3                                                        ______________________________________                                          .sup.1 The capped polyisocyanate crosslinker was prepared from the             following mixture of ingredients:                                        

    ______________________________________                                         Ingredients      Parts by weight                                               ______________________________________                                         Polyisocyanate.sup.a                                                                            1325.00                                                       Methyl isobutyl ketone                                                                          221.81                                                        2-(2-Butoxyethoxy)ethanol                                                                       324.46                                                        Dibutyltin dilaurate                                                                            0.2                                                           2-Butoxy ethanol 945.44                                                        ______________________________________                                          .sup.a Polymeric MDI available from Miles Inc. as MONDUR MR as noted in        Example 1A.                                                                    The polyisocyanate, methyl isobutyl ketone and dibutyltin dilaurate were       charged to a reaction flask under a nitrogen atmosphere.                       2(2-butoxyethoxy)ethanol was added slowly allowing the reaction to             exotherm to a temperature between 45 to 50° C. Upon completion of       the addition the reaction mixture was held at 50° C. for 30             minutes. 2butoxy ethanol then was added and the mixture allowed to             exotherm 110° C. and held there until Infrared analysis indicated       no unreacted NCO remained                                                      .sup.2 Diketimine derived from diethylenetriamine and methyl isobutyl          ketone (73% solids in methyl isobutyl ketone).                           

The EPON 828, initial charge of Bisphenol A-ethylene oxide adduct, Bisphenol A and the initial charge of methyl isobutyl ketone were charged to a reaction vessel and heated under a nitrogen atmosphere to 125° C. Ethyl triphenyl phosphonium iodide then was added and the reaction mixture allowed to exotherm to about 145° C. The reaction was held at 145° C. for 2 hours and the second charge of Bisphenol A-ethylene oxide adduct was added and an epoxy equivalent was obtained. Epoxy equivalent usually stalls close to the target epoxy equivalent weight. At this point, the second charge of methyl isobutyl ketone, the crosslinker, the diketimine and N-methylethanolamine were added in succession. The mixture was allowed to exotherm and then a temperature of 125° C. was established. The mixture was held at 125° C. for 1 hour. The resin mixture (7500 parts) was dispersed in aqueous medium by adding it to a mixture of 165.59 parts of sulfamic acid and 4908.21 parts of deionized water. After 60 minutes, the dispersion was further thinned with 2794.18 parts of deionized water and 2830.95 parts of deionized water in stages and vacuum stripped to remove organic solvent to give a dispersion having a solids content of 42.53 percent and a particle size of 830 Angstroms.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         Main vehicle prepared above                                                                      1329.2                                                       Co-resin 1 of Example IA, at                                                                     170.6                                                        35.3% solids                                                                   Butyl CARBITOL formal                                                                            37.2                                                         plasticizer                                                                    Co-resin 2 of Example IA, at                                                                     73.5                                                         18.4% solids                                                                   Deionized water   1990.1                                                       E6066 paste       193.4                                                        Total             3800.0                                                       ______________________________________                                    

EXAMPLE VIII-B

This example describes the preparation of a cationic electrodeposition bath containing 0.5% oleic acid on main vehicle solids.

A main vehicle was prepared from the following ingredients.

    ______________________________________                                         Ingredients        Parts by weight                                             ______________________________________                                         EPON 828           614.68                                                      Bisphenol A-ethylene oxide                                                                        125.00                                                      adduct (1/6 molar ratio)                                                       Bisphenol A        265.42                                                      Methyl isobutyl ketone                                                                            20.51                                                       Ethyltriphenyl phosphonium                                                                        0.6                                                         iodide                                                                         Bisphenol A-ethylene oxide                                                                        125.00                                                      adduct (1/6 molar ratio)                                                       Methyl isobutyl ketone                                                                            87.22                                                       Crosslinker of Example VIII-A                                                                     693.55                                                      Diketimine         54.99                                                       N-methyl ethanol amine                                                                            46.96                                                       ______________________________________                                    

The reaction was performed as in Example VIII-A, except that after the second exotherm a temperature of 130° C. was established. The mixture was held at 130° C. for 1 hour. The resin mixture (1600 parts) was dispersed in aqueous medium by adding it to a mixture of 34.17 parts of sulfamic acid and 1052.03 parts of deionized water. After 60 minutes, 7.20 parts of Emersol 210 oleic acid (a commercial grade of oleic acid available from Emery Chemicals Group of Henkel Corporation) was added to the high solids dispersion and further mixed for 30 minutes. The dispersion was further thinned with 598.53 parts of deionized water and 606.41 parts of deionized water in stages and vacuum stripped to remove organic solvent to give a dispersion having a solids content of 43.0 percent and a particle size of 948 Angstroms.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         Main vehicle prepared above                                                                      2627.5                                                       Co-resin 1 of Example IA at                                                                      341.6                                                        35.3% solids                                                                   Butyl CARBITOL formal                                                                            74.4                                                         plasticizer                                                                    Co-resin 2 of Example IA at                                                                      147.0                                                        18.4% solids                                                                   Deionized water   4022.7                                                       E6066 paste       386.8                                                        Total             7600.0                                                       ______________________________________                                    

EXAMPLE VIII-C

This example describes the preparation of a cationic electrodeposition bath containing 0.5% of gum rosin (natural abietic acid) on main vehicle solids.

A main vehicle was prepared from the following ingredients:

    ______________________________________                                         Ingredients        Parts by weight                                             ______________________________________                                         EPON 828           106.2                                                       Bisphenol A-ethylene oxide                                                                        21.6                                                        adduct (1/6 molar ratio)                                                       Bisphenol A        45.9                                                        Methyl isobutyl ketone                                                                            5.4                                                         Ethyltriphenol phosphonium                                                                        0.1                                                         iodide                                                                         Bisphenol A-ethylene oxide                                                                        21.6                                                        adduct (1/6 molar ratio)                                                       Methyl isobutyl ketone                                                                            13.0                                                        Crosslinker of Example VIII-A                                                                     120.3                                                       Diketimine         9.8                                                         N-methyl ethanol amine                                                                            8.4                                                         ______________________________________                                    

The reaction was performed as in Example VIII-A, except that after the second exotherm a temperature of 130° C. was established. The mixture was held at 130° C. for 1 hour. The resin mixture (345.3 parts) was dispersed in aqueous medium by adding it to a mixture of 7.62 parts of sulfamic acid and 227.2 parts of deionized water. After 60 minutes 1.6 parts of Gum Rosin available from the Colyer Chemical Company and 1.6 parts of methyl isobutyl ketone premixed was added as a solution to the high solids dispersion and further mixed for 30 minutes. This gum rosin contains 10% neutral materials and 90% rosin acid of which 90% is abietic acid (and isomers) and 10% is a mixture of dihydroabietic acid and dehydroabietic acid. The dispersion was further thinned with 129.3 parts of deionized water and 109.4 parts of deionized water in stages and vacuum stripped to remove organic solvent to give a dispersion having a solids content of 40.8 percent and a particle size of 924 Angstroms.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         Main vehicle prepared above                                                                      2769.2                                                       Co-resin 1 of Example IA at                                                                      341.6                                                        35.3% solids                                                                   Butyl CARBITOL formal                                                                            74.4                                                         Co-resin 2 of Example IA at                                                                      147.0                                                        18.4% solids                                                                   Deionized water   3881.4                                                       E6066 paste       386.8                                                        Total             7600.0                                                       ______________________________________                                    

EXAMPLE VIII-D

This example describes the preparation of a cationic electrodeposition bath containing 0.3% of gum rosin (natural abietic acid) on main vehicle solids.

A main vehicle dispersion was prepared as in Example VIII-C, having a solids content of 41.3 percent and a particle size of 932 Angstroms. The dispersion differed from that of Example VIII-C in that it contained 0.3% gum rosin on main vehicle solids instead of 0.5%.

A cationic electrodeposition bath was prepared from the following ingredients:

    ______________________________________                                         Ingredients       Parts by weight                                              ______________________________________                                         Main vehicle prepared above                                                                      2735.7                                                       Co-resin 1 of Example IA at                                                                      341.6                                                        35.3% solids                                                                   Butyl CARBITOL formal                                                                            74.4                                                         plasticizer                                                                    Co-resin 2 of Example IA at                                                                      147.0                                                        18.4% solids                                                                   Deionized water   3914.9                                                       E6066 paste       386.8                                                        Total             7600.0                                                       ______________________________________                                    

The baths of Examples VIII-A through VIII-D were each ultrafiltered, removing 20% of the total weight of the bath as ultrafiltrate and replacing the ultrafiltrate with deionized water. Smooth zinc phosphated steel panels and smooth unphosphated electrogalvanized steel panels were electrocoated with each composition at 275 volts for 2 minutes at bath temperatures of 81°-86° F. (27.2°-30.0° C.). After rinsing with deionized water, the panels were baked for 30 minutes at 310° F. (154.5° C.), 325° F. (162.7° C.), or 340° F. (171.1° C.). Resulting film builds were about 0.9 mils (22.9 microns). The cured coatings were measured for appearance, cure response as measured by acetone resistance and Thermo-Gravimetric Analysis (TGA), humidity resistance over electrogalvanized substrate, and resistance to warm salt solution over electrogalvanized substrate.

All test results are summarized on Table VIII.

                                      TABLE VIII                                   __________________________________________________________________________               Wet                                                                            Substrate         Humidity                                                                               Warm Salt Solution                                   Rupture Acetone   Resistance.sup.5                                                                       Resistance.sup.6                           Example                                                                             Additive                                                                            Rating.sup.1                                                                        R.sub.A .sup.2                                                                    Resistance.sup.3                                                                     TGA.sup.4                                                                          325° F.                                                                     340° F.                                                                     325° F.                                                                      340° F.                        __________________________________________________________________________     VIII-A                                                                              None 10   10.40                                                                             12    105 10  10  5 mm.                                                                               5 mm.                                 VIII-B                                                                              0.5% oleic                                                                          6    8.10                                                                              >100  238 0   0   complete                                                                            complete                                   acid         (softens)         adhesion                                                                            adhesion                                                                  loss loss                                  VIII-C                                                                              0.5% gum                                                                            7.5  7.21                                                                              >100 (very                                                                           334 10  10  5 mm.                                                                               4 mm.                                      rosin        slightly                                                                       softens)                                                     VIII-D                                                                              0.3% gum                                                                            9    7.28                                                                              >100  252 7   10  3.5 mm.                                                                             3.5 mm.                                    rosin        (softens)                                                    __________________________________________________________________________

Example VIII demonstrates that in the electrodepositable composition of the present invention, abietic acid or gum rosin is significantly better than oleic acid for preventing rupturing on wet substrates, and for improving adhesion to bare electrogalvanized substrate, and is the preferred embodiment of the invention with respect to these properties. Gum rosin is slightly better than oleic acid for appearance and cure response. The example also demonstrates that 0.3% gum rosin on main vehicle solids has effects on cure response approximately equivalent to 0.5% oleic acid, while providing a further improvement in resistance to rupturing defects over wet substrate. 

We claim:
 1. In a method of electrocoating an electroconductive substrate which serves as a cathode in an electrical circuit comprising said cathode and an anode immersed in an aqueous electrodepositable composition containing a cationic water dispersible resin, said method comprising passing an electric current between the anode and the cathode to cause the electrodepositable composition to deposit on the cathode as a substantially continuous film, and heating the electrodeposited film at an elevated temperature to cure the film, wherein the electrodepositable composition comprises (a) an active hydrogen-containing cationic resin electrodepositable on a cathode; (b) a capped polyisocyanate curing agent; and (c) an organotin-containing catalyst; the improvement comprising the addition to the electrodepositable composition of at least one water immiscible acid functional compound having a hydrocarbon chain of at least 5 carbon atoms selected from the group consisting of abietic acid and natural sources of abietic acid.
 2. The method of claim 1 in which the cationic resin is derived from a polyepoxide.
 3. The method of claim 1 wherein the cathode is a steel substrate.
 4. The method of claim 2 in which the polyepoxide is a polyglycidyl ether of a polyhydric alcohol.
 5. The method of claim 2 in which the cationic resin contains salt groups which are amine salt groups.
 6. The method of claim 5 in which the amine salt groups are derived from basic nitrogen groups neutralized with an acid selected from the group consisting of formic acid, acetic acid, lactic acid, phosphoric acid, sulfamic acid, and mixtures thereof.
 7. The method of claim 1 in which the acid functional compound is gum rosin.
 8. The method of claim 1 in which the acid functional compound is a carboxylic acid.
 9. The method of claim 1 in which the acid functional compound is polycyclic.
 10. The method of claim 9 in which the acid functional compound is abietic acid.
 11. The method of claim 1 in which the organotin-containing catalyst is present in amounts of about 0.05 to 1 percent tin by weight, based on the total weight of resin solids in the electrodepositable composition.
 12. The method of claim 1 wherein the electrodepositable composition contains lead.
 13. The method of claim 1 in which the electrodeposited film is heated to a temperature range of about 300° to 340° F. (148.8° to 171.1° C.) to cure the film.
 14. The method of claim 1 wherein the addition of acid functional compound is in an amount ranging from about 0.1 to 3.0 percent by weight based on the weight of the main vehicle resin solids of the active hydrogen-containing cationic resin and the capped polyisocyanate curing agent.
 15. The method of claim 14 wherein the acid functional compound is present in an amount ranging from about 0.4 to 1.5 percent by weight based on the weight of the main vehicle resin solids so that a reduced amount of the organotin-containing catalyst is present in amounts of about 0.05 to 0.5 percent tin by weight, based on weight of resin solids.
 16. The method of claim 1 wherein the acid functional compound is present from the addition of the acid functional compound to the electrodepositable composition and wherein the acid functional compound remains unreacted with the cationic resin backbone of the active hydrogen-containing cationic resin in the electrodepositable composition to enable the acid functional compound to enhance the cure response when the organotin catalyst activates cure of the electrodeposition composition.
 17. The method of claim 1 wherein the polyisocyanate curing agent is present in the amount ranging from about 5 to 60 percent by weight based on total weight of resin solids.
 18. The method of claim 17 wherein the polyisocyanate curing agent is present in the amount ranging from about 25 to 50 percent by weight based on total weight of resin solids.
 19. In an electrodepositable composition comprising (a) an active hydrogen-containing cationic resin electrodepositable on a cathode; (b) a capped polyisocyanate curing agent; and (c) an organotin-containing catalyst; the improvement comprising the presence in the electrodepositable composition of at least one water immiscible acid functional compound having a hydrocarbon chain of at least 5 carbon atoms including abietic acid and natural sources thereof.
 20. The electrodepositable composition of claim 19 in which the cationic resin is derived from a polyepoxide.
 21. The electrodepositable composition of claim 20 in which the polyepoxide is a polyglycidyl ether of a polyhydric alcohol.
 22. The electrodepositable composition of claim 20 in which the cationic resin contains salt groups which are amine salt groups.
 23. The electrodepositable composition of claim 22 in which the amine salt groups are derived from basic nitrogen groups neutralized with an acid selected from the group consisting of formic acid, acetic acid, lactic acid, phosphoric acid, sulfamic acid, and mixtures thereof.
 24. The electrodepositable composition of claim 19 in which the acid functional compound is a monocarboxylic acid.
 25. The electrodepositable composition of claim 19 in which the acid functional compound is polycyclic.
 26. The electrodepositable composition of claim 1 in which the organotin-containing catalyst is present in amounts of about 0.05 to 1 percent tin by weight, based on the total weight of resin solids in the electrodepositable composition.
 27. The electrodepositable composition of claim 26 further comprising lead.
 28. The electrodepositable composition of claim 19 which is curable at a temperature range of about 300° to 340° F. (148.8° to 171.1° C.) 